Model |
Fireproof material |
Density（g/cm3） |
Floatability（24H≥） |
PH |
Application |
|
CTL-901 |
Talcum powder |
1.25-1.35 |
99 |
8-10 |
Cast aluminum |
|
CTL-902 |
Alumina powder |
1.45-1.50 |
99 |
8-10 |
Cast iron |
|
CTL-903 |
Alumina powder
Zircon flour |
1.50-1.56 |
99 |
8-10 |
Cast iron |
|
CTL-904 |
Zircon flour |
1.75-2.00 |
98 |
8-10 |
Cast steel |
|
CTL-905 |
Forsterite |
1.60-1.80 |
98 |
8-10 |
High manganese steel |
|
Method of application |
Dilute the agent to desired comdition, shake it uniformly, and adopt the following processes: brushing,soaking or pouring, dry it by itself, or oven the surface coat at the temperature of 50℃ or so.When it is required to use the powdery agent, stir it at medium speed for 2-3h, filling proper amount of water. Do not use the stirred agent before adding ration of deflocculating agent, stirring it for 30 min and laying it aside for half an hour. Keep stirring the agent while spplying it. |
|
Performance and state |
The agent can be shelled out after sintering at medium level.Polish and smooth surface. It has the advantages of no crack with urgent heating, no toxicity and odor, good floatability and gas permeability, quick hardening and heat insulation. |
|
Precautions |
Pay attention to freeze protection in winter,anticorrosion in summer, fire protection and use it within warranty period. |
|
Packages |
35kg |
|
|